MAGNELiTE
U.S.A is a result of American Building
Technologies Inc's continued endeavor
to offer quality products to the
building industry. MAGNELiTE U.S.A
Magnesium Silicate Boards is a Non-Combustible
BS 476 - Part 4 Class 1 certified
building board capable of providing
up to 3 hours of fire rating. It
is an all-weather, high strength,
non-combustible, fire resistant
board for interior and exterior
applications. MAGNELiTE U.S.A has
100% asbestos free composition manufactured
from a matrix of inorganic materials
like natural silicates, CaCO3, MgO
and reinforced with glass fiber.
The innovative manufacturing technology
of multiple glass fiber reinforcements
provides the board with exceptional
flexibility and strength. MAGNELiTE
U.S.A is also available in special
finishes of stone, brick and natural
veneer laminates.
"Come fire, Come moisture,
Come heat, Come termites, MAGNELiTE
U.S.A fights it all and is a one
solution building board."
|
 |
|
|
|
|
|
|
|
|
MMS-223
|
MMS-237
|
MMS-225
|
|
|
|
|
|
MMS-238
|
MMS-227
|
MMS-216
|
|
|
|
 |
Up
to 3 hours fire rated, non-combustibility |
 |
Superior
moisture resistance |
 |
Highly
resistant to vermin and termite attack |
 |
Chemically
stable |
 |
Dimensionally
stable |
 |
Resistant
to climatic conditions and moisture |
 |
Good
thermal properties |
 |
Easy
to work and fix |
 |
Safe
to work with, containing no hazardous
materials and 100% asbestos free |
|
| Mechanical
& Physical Properties |
| Density
(Ave.) |
1050
Kg/m3 |
|
Bending
Strength
Dry
Saturated
|
> 7MpA
> 7MpA |
| Moisture
Content |
About
13.2% |
| Moisture
Absorption (After 24 hours soak) |
32% |
| Moisture
Absorption Expansion Rate |
< 0.09% |
| Thermal
Conductivity |
0.139
W/mK 0.106 Kcal/m hr °C |
| Surface
Alkalinity |
Between
9.5 - 10 pH |
| Sound
Absorption |
38dB
(93mm partition) 100 - 8000Hz frequency |
| Bonding
Agent |
Magnebond
is an odorless bonding agent and free
from formaldehyde |
|
| Dimensional
Tolerance |
| Description |
Tolerance
(mm) |
| Thickness
|
(mm)
0.2mm, +0.4mm |
| Width
|
1mm,
+2mm |
| Length
|
1mm,
+3mm |
| Squareness
|
<
5mm |
|
| Fire
Resistance |
| MAGNELiTE
U.S.A Magnesium Silicate Board
will not burn. It has been tested
to : |
| (1)
BS 476 Part 4 |
Non
Combustibility |
| (2)
BS 476 Part 7 |
Surface
Spread of flame as CLASS 1 classification |
| (3)
EN-ISO 1716 |
Bomb
calorimeter test to European standard |
| (4)
EN-ISO 1182 |
Non
Combustibility to European standard,
rated as CLASS - A1 material |
|
|
WATER
ENDURANCE TEST
No bloating, swelling or delamination
of the board when board tested under water.
FREEZE
/ THAW TEST
Frozen at -17.55C ± 2.55C for over 16
hours, kept frozen at 17.55C for 4 hours.
Thawed by immersing in water at approximate
200C, maintained at temperature of 200C
± 33C for 5 hours. Freeze and thaw cycle
is repeated for 10 times. TEST RESULT
: No cracking, disintegration, crumbling,
stripping occurs on the MAGNELiTE U.S.A
Magnesium Silicate Board.
|
|
| |
 |
|
|